Method and product for varying the thickening time of a class g cement used in completing a subterranean wellbore

ABSTRACT

Spent Claus catalyst having a high alumina content is used as an ingredient in the manufacture of Portland cements in place of all or a portion of a conventional source of alumina. The spent Claus catalyst is preferably of a small particle size and can be ground to the desired fineness before mixing with the other ingredients that are heated in a conventional kiln to produce the cement composition. Finely ground spent Claus catalyst can also be used as an additive at levels of 0.1% to 2% by weight to increase the thickening time of shallow casing cement slurries.

FIELD OF THE INVENTION

This invention relates to the use of spent Claus catalyst particles in the production of Portland cement.

BACKGROUND OF THE INVENTION

The Claus process continues to be the most widely used process worldwide to convert hydrogen sulfide that has been stripped from acid gas or refinery off-gas streams to elemental sulfur. It consists of a two-stage process: the first process stage is thermal and the second stage is catalytic. During the thermal process, the H₂S is partially oxidized with air in a reaction furnace at high temperatures, e.g., from 1000°-1400° C. Sulfur is formed, but some H₂S remains unreacted and SO₂ is also formed, as depicted below:

2H₂S+3O₂→2SO₂+2H₂O  (I)

During the catalytic process, the remaining H₂S is reacted with the SO₂ at lower temperatures, i.e., about 200°-350° C., over a catalyst to produce additional elemental sulfur, as follows:

2H₂S+SO₂→3S_(x)+2H₂O  (II)

The Claus catalyst which offers improved sulfur conversion over spherical activated bauxite, or alumina, has high surface area, low density and high macroporosity. These properties provide maximum activity for the conversion of sulfur compounds. The art relating to the production of Claus catalysts is well developed, as shown, for example, in U.S. Pat. No. 4,364,858 and the numerous patents cited and discussed there. However, the reaction does not go to completion, even with the best catalyst. For this reason, two or three catalytic stages are used, with sulfur being removed between the stages.

Claus catalyst is deactivated due to lay down of coke and sulfur-containing species causing lowering of sulfur recovery and also polluting the atmosphere by releasing excessive amounts of sulfur dioxide during acid gas flaring. The deactivation of the Claus catalyst is caused by a variety of factors, such as the presence of accompanying hydrocarbons, particularly of C-5's and benzene, toluene and xylenes. Sour gases are prone to lay down coke on Claus catalyst due to thermal cracking in the split-flow mode.

Hundreds of tons/year of spent Claus catalyst are produced by gas processing plants, gas-oil separation plants (GOSPs) and natural liquid gas fractionation facilities due to frequent replacement of the alumina catalyst beds. In many instances, the spent catalyst has been disposed of by dumping it in a landfill. The cost of landfilling spent Claus catalyst is generally minimal where the land is available and inexpensive, the principal cost being its transportation.

National and international regulations have provided increased opportunities and economic incentives for the petroleum and gas processing industries to implement waste reduction programs for the purpose of enhancing the environment. The incentives for waste minimization on an international basis have been increased by the ban on the land disposal of untreated wastes from the petroleum industry. As the complexity and cost of waste management and disposal increases, waste minimization becomes a significant priority for industry and government.

The goal of reducing waste material from industrial processes requiring disposal can be accomplished either by regeneration of the material or by finding a new and economical use for the spent Claus catalyst waste material.

In some instances, the regeneration treatment cost has been found to be more expensive than purchasing fresh catalyst and, therefore, regeneration was not economically viable.

Other proposals for utilizing spend catalytic materials in an environmentally acceptable manner can also be found in the prior art. For example, U.S. Pat. No. 5,032,548 and U.S. Pat. No. 5,096,498 recommend the use of catalyst particles within a prescribed size range as a base in large construction projects, such as roads and levees. However, the spent catalyst must also be mixed with hydrated lime, Portland cement and other binders.

The use of spent catalyst fines admixed with concrete is disclosed in U.S. Pat. No. 4,231,801. The use of catalyst particles in the process for manufacturing a Portland cement prior to the burning step is disclosed, but it also teaches the addition of an agglomerating material.

It is therefore a principal object of the present invention to provide a means of economically and beneficially utilizing the spent Claus catalyst in order to provide an alternative to landfill disposal.

A further object of the invention is to provide new uses for spent Claus catalyst that will have a significant favorable environmental and cost-saving impact on those industries that must dispose of the spent catalyst.

SUMMARY OF THE INVENTION

The above objects and other advantages are achieved by the method and composition of the invention that broadly contemplates the addition of spent Claus catalyst as an additive, or raw material, in the manufacture of Type I, II and V Portland cement.

The spent Claus catalyst is comprised principally of alumina, or Al₂O₃. This compound is an essential additive for the production of Portland cement, which contains about 5% of alumina.

Portland cement is composed of lime or limestone, alumina, iron oxide and silica and is manufactured by burning all of these materials in pre-determined is proportions in a rotary kiln at temperatures in the range of 1450°-1500° C. Small amounts of magnesia, sodium, potassium and sulfur are also present. The principal reactions are represented by the following:

CaCO₃(limestone)→CaO+CO

7CaO+Al₂Si₂O₇→Ca₂SiO₄+Ca₃Al₂O₆

The product formed in the kiln is known as clinker. The clinker is allowed to cool and then is ground to a fine powder along with a small percentage (4-5%) of gypsum or its derivatives. This finely blended powder is known as Portland cement.

The silica can be provided from a number of sources, including clay, sand, quartz, and other materials that are well known in the art. A portion of the alumina-containing material is replaced by the spent Claus catalyst.

Spent Claus catalyst utilization in the production of Portland cement will provide significant environmental and cost-saving benefits since the volume of cement manufacturing and use in the areas where the spent Claus catalyst is generated will likely be sufficient to utilize all or a significant proportion of this waste material, thereby eliminating the need for landfill disposal of the spent catalyst.

In this application of the invention, the spent catalyst may contain residual hydrocarbons that will be released and/or oxidized during heating in the kin. Should tests of the finished cement and/or its concrete products indicate the presence of residual hydrocarbons, the end use applications should exclude closed structures used by personnel and animals due to the potential presence of such hydrocarbons. Alternatively, the spent Claus catalyst can be treated thermally and/or chemically to remove, or reduce to an acceptable level, any hydrocarbons that may originally have been be present.

DETAILED DESCRIPTION OF THE INVENTION

The methods and compositions of the preferred embodiments of using the spent Claus catalyst are described in the context of the examples which follow. These examples are directed to the utilization of spent Claus catalyst as a raw material in the manufacture of Types I, II and V cement.

In preparing the representative samples for this embodiment of the process and product of the invention, spent Claus catalyst having a high alumina content was blended with other conventional ingredients to manufacture a Portland cement of the type used in the construction of infrastructure and other building projects. The cured concrete product was acceptable in terms of its physical performance characteristics.

In order to determine the composition of spent Claus catalyst particles, four spent Claus catalyst samples from different petroleum processing plants and processes were analyzed utilizing X-ray fluorescence spectrometry. The catalysts were presumed to be from different batches and may have been from different commercial producers. Each of the samples was ground in an agate pulverizer to a fineness of about 100 mesh and mixed thoroughly before being exposed to the X-ray beam. These samples were composed mainly of aluminum, carbon, sulfur, hydrocarbon and traces of other metals. Sample A contained higher aluminum oxide content and less carbon and hydrocarbon components when compared to other spent catalyst samples. The alumina content of the samples ranged from about 74% to 84% by weight.

The composition in weight percent of four spent Claus catalysts as received are reported in Table 1.

TABLE 1 Sample 1 Sample 2 Sample 3 Sample 4 Compound Wt % Wt % Wt % Wt % SiO₂ <.01 <.01 <.01 0.01 Al₂O₃ 83.74 74.84 75.31 74.35 Fe₂O₃ <.01 <.01 <.01 <.01 CaO 0.09 0.08 0.07 0.08 MgO 0.23 0.20 0.20 0.20 SO₃ 0.09 0.27 0.29 0.20 Na₂O 0.28 0.25 0.26 0.25 K₂O <.01 <.01 <.01 <.01 TiO₂ <.01 <.01 <.01 <.01 P₂O₅ <.01 <.01 <.01 <.01 Mn₂O₃ 0.01 0.01 0.01 0.01 SrO 0.02 0.02 0.02 0.02 Cr₂O₃ <.01 <.01 <.01 <.01 ZnO 0.01 0.01 0.01 0.01 L.O.I. (950° C.) 15.54 23.99 23.61 24.44 Total 100.01 99.66 99.77 99.56 The Loss on Ignition (L.O.I.) reported above was conducted at 950° C.

Four different cement formulations were prepared using the four different spent Claus catalysts Samples 1-4 that are composed mainly of alumina, and were mixed with limestone, sand, clay and iron ore. A fifth (control) mix was prepared from conventional raw materials to produce five typical U.S. type V cements. The tests were conducted at an independent laboratory and are reported in Table 2. The quantities of each ingredient are in grams.

TABLE 2 Control Mix 1 Mix 2 Mix 3 Mix 4 Limestone 1287 1362 1365 1365 1365 Clay 232 0 0 0 0 Iron Ore 26 35 35 35 35 Sand 0 113 113 113 113 Spent Claus Catalyst 0 30 30 30 30 Total 1545 1540 1543 1543 1544 The projected mineralogical composition of clinkers, as a percentage (%), is shown in Table 3.

TABLE 3 Typical Range Control Mix 1 Mix 2 Mix 3 Mix 4 C₃S tricalcium 43 to 70 60.0 60.0 61.9 60.8 60.0 silicate C₂S dicalcium 11 to 31 16.6 16.3 16.0 16.1 17.0 silicate C₃A tricalcium 0 to 5 3.6 4.0 4.3 4.3 4.3 aluminate C₄AF 10 to 19 10.9 10.9 12.1 12.2 12.2 tetracalcium aluminoferrite

The materials utilized in the formulations of Table 2 were crushed, blended and ground in a porcelain jar mill to the fineness of 85% passing a 76 μm sieve. Briquettes of about 100 grams each were prepared in a Carver hydraulic press. The specimens were pre-heated at 900° C. and fired at 1450° C. in a Blue M high-temperature furnace.

After firing, the clinker briquettes having the composition of Table 3 were crushed and ground to a Blaine specific surface of 340 m²/Kg with an addition of 5% Terra Alba gypsum. The resulting cements were analyzed by XRF. The results of this analysis of the cement chemical composition, as wt %, is reported in Table 4.

TABLE 4 Control Mix 1 Mix 2 Mix 3 Mix 4 SiO₂ 20.44 20.85 20.41 21.11 21.54 Al₂O₃ 3.47 4.22 4.07 4.18 4.20 Fe₂O₃ 3.61 4.00 3.98 4.07 4.10 CaO 64.32 63.76 64.86 63.98 63.69 MgO 2.34 1.90 1.87 1.94 1.98 SO₃ 2.56 2.49 2.56 2.60 2.59 Na₂O 0.20 0.09 0.09 0.09 0.10 K₂O 0.31 0.26 0.25 0.26 0.25 TiO₂ 0.21 0.13 0.13 0.14 0.14 P₂O₅ 0.03 0.02 0.02 0.02 0.02 Mn₂O₃ 0.04 0.04 0.04 0.04 0.04 SrO 0.04 0.04 0.04 0.04 0.04 Cr₂O₃ <.01 <.01 <.01 <.01 <.01 ZnO <.01 <.01 <.01 <.01 <.01

The resulting cements were tested for compressive strength in mortar cubes according to ASTM C 109, the results of which are reported in Table 5. The mortar cube strength is in psi.

TABLE 5 Control Mix 1 Mix 2 Mix 3 Mix 4 3 days 2440 2280 2260 2380 2450 7 days 3620 3080 3140 3010 3300 28 days  4620 4670 4630 5020 5210

The data in Table 5 shows some variations in the strength of cement specimens, but these variations are not significant and the specimens are considered to be of substantially the same quality. It is evident that replacement of clay with the Claus catalyst sand mix did not negatively affect the cement's performance.

Another analysis was carried out to evaluate burnability of the four mixing formulations. Burnability is the term used to indicate the reactivity of the kiln feed with respect to forming clinker minerals during the burning process, and is usually measured by the free lime content of the clinker. The lower the temperature at which the targeted free lime can be obtained, the better is the burnability of the kiln feed. One procedure for characterizing the burnability of a kiln feed is to perform laboratory burns under standardized conditions and to then analyze for the resulting free lime content

Results from such tests can then be compared, and the raw materials and mix compositions giving the best burnability values can be selected by comparison. Burnability can also be predicted by the chemical and mineralogical parameters of the raw mix.

The burnability of the five mixes described above was evaluated according to the equations developed by F. L. Smidth as follows:

FL₁₄₀₀=0.31(LSF−I00)+2.18(Ms−I.8)+0.73Q ₄₅+0.33C ₁₂₅+0.34A ₄₅  (1)

FL₁₅₀₀=0.2I(LSF−I00)+I.59(Ms−I.8)+0.40Q ₄₅+0.22C ₁₂₅+0.08A ₄₅  (2)

Where:

-   -   FL₁₄₀₀=“Virtual burnability index”, or free lime content         anticipated in a commercial clinker fired at 1400° C.;     -   FL₁₅₀₀=same, at 1500° C.;     -   LSF=lime saturation factor;     -   Ms=silica ratio;     -   Q₄₅32% of quartz>45 μm;     -   C₁₂₅32% of calcite>125 μm; and     -   A₄₅32% of insoluble particles>45 μm.

The importance of this determination is its use in evaluating the effect of possible changes in (1) chemical composition, or (2) mineralogy and fineness, or (3) both.

Both analytical and direct empirical approaches were used. For determination of the parameters included in the equations (1) and (2), the chemical parameters of the lime saturation factor and silica ratio were taken from the chemical analyses. For measurement of the particle sizes, the material was screened through Nos. 120 and 325 mesh sieves, being 125 and 45 μm, respectively. The +45 μm residue was treated with acetic acid to dissolve the carbonate particles. The residues were examined microscopically by a point-count technique and the particle sizes in raw mixes are reported in Table 6.

TABLE 6 Control Mix I Mix 2 Mix 3 Mix 4 Residue >125 μm 1.4 5.8 6.3 6.0 6.2 Calcite in residue 76.3 50.3 54.3 55.3 56.3 Calcite >125 μm in total 1.1 2.9 3.4 3.3 3.5 sample >45 μm residue (acid wash) 5.2 9.7 9.4 10.2 10.1 Quartz in residue 26.6 36 42.3 38.6 29 Acid-insoluble particles 73.4 64 57.7 61.4 71 >45 μm in residue Quartz >45 μm in total 1.4 3.5 4 3.9 2.9 sample Other acid-insoluble 3.8 6.2 5.4 6.3 7.2 particles >45 μm in total sample The results of calculations are shown in Table 7 as the virtual burnability index of the mixes

TABLE 7 FL Control Mix 1 Mix 2 Mix 3 Mix 4 1400 2.87 5.81 6.07 6.27 5.91 1500 1.32 2.75 3.00 3.01 2.72

Direct free lime determination was conducted using the following procedure. Raw meal pellets of about 13 mm in size were prepared and dried, and pre-calcined at 900° C. The pellets were further fired at 1350° C., 1400° C. and 1450° C. for 20 minutes in an electric furnace. Free CaO, or free lime content was analyzed as the principal criterion of the lime digestion which is reported in Table 8. The fired samples were also subjected to microscopic examination as will be described below.

TABLE 8 ° C. Control Mix 1 Mix 2 Mix 3 Mix 4 1350 0.76 1.48 2.26 1.54 1.5 1400 0.42 0.72 0.69 0.58 0.74 1450 0.35 0.50 0.51 0.43 0.60

When analyzing the data from Tables 7 and 8, it is to be noted that, due to the vastly different firing conditions in a commercial kiln and a laboratory furnace, the “virtual burnability” values in Table 7 are not identical to the actual free lime in Table 8. However, the values clearly demonstrate the trends in the burnability of the mixes. In the experimental burns, all mixes produced equally acceptable results. However, the data indicates that the control mix possessed better burnability characteristics due to the finer sizes of quartz and silicate particles. Generally, poor quartz grindability can lead to the necessity of finer grinding raw materials containing sand and similar ingredients to avoid problems in burning.

Microscopic examination was also undertaken to detect any irregularities in the clinker formation. The purpose of this microscopic examination was to assist in the selection of the proportions of ingredients in the final cement formulations. For the purpose of this examination, the samples were identified as set forth in Table 9.

TABLE 9 Sample ID Mix Temperature, ° C. C-135 Control 1350 C-140 Control 1400 C-145 Control 1450 1-135 1 1350 1-140 1 1400 1-145 1 1450 2-135 2 1350 2-140 2 1400 2-145 2 1450 3-135 3 1350 3-140 3 1400 3-145 3 1450 4-135 4 1350 4-140 4 1400 4-145 4 1450

The results of the microscopic examination indicated that spent Claus catalysts samples using clay did not lead to any abnormalities in the clinker microstructure. Certain characteristics such as non-uniform distribution and formation of belite nests can be attributed to the relatively coarse sizes of the quartz grains. Under actual production conditions, the meal fineness can be adjusted to accommodate the compositional changes.

As will be understood from the above description and data, spent Claus catalyst can be successfully used to produce a high quality Portland cement for use in the construction of facilities of various types. No special processing is required prior to addition of the spend Claus catalyst to the Kiln and the processing and handling of the clinkers can continue as with the prior art formulations. The invention thus meets the objectives of disposing of significant quantities of a material that has been considered a waste by-product of the petroleum refining industry in an economical and environmental acceptable manner.

A further aspect of the invention is directed to the use of spent Claus catalyst particles as an additive to modify the curing characteristics of an oilwell cement slurry for shallow casing cementing.

It has been found that when spent Claus catalyst is added to shallow is casing cement slurries, there is an increase in the thickening time of the shallow casing cement slurry, as measured by API10 procedures. The observed increase in thickening time occurred at additive levels of 0.1% and 2.0% of the spent catalyst.

In the practice of this preferred embodiment of the invention, the spent catalyst was ground or pulverized to particles in the size range of from 6.8-10.4 microns (μm) before addition to the slurry.

Table 10 reports the data from the evaluation of oilwell slurry cement samples with and without the additive.

TABLE 10 Properties Sample A Sample B Sample C Sample D Blank CI-G SACK 1.00 1.00 1.00 1.00 1.00 TWTR % VOL 100 100 100 100 100 SCC Additive 0.100 1.00 2.00 5.00 0.00 % BWOC Thickening Increase Decrease Increase Decrease 105 Time - minutes −119

Blending spent catalyst into the cement slurry of shallow casing cement jobs gives an increase in the thickening time to 119 minutes compared to 105 minutes for unmodified class G cement formulations.

In order to adapt this spent catalyst for use as an additive in oilwell cement, the combined mixture of oilwell cement and spent catalyst must be easily pumpable for a sufficient time to allow proper placement of the slurry in the well. The desired consistency for the pumpable cement can be achieved by pulverizing the spent catalyst, which is in spherical form, to fine particles in the range of about 6.8-10.4 μm.

Although the above examples and description is comprehensive, it is intended to be illustrative and various modifications to the methods and compositions described will be apparent to those of ordinary skill in the art. The full scope of the invention is therefore to be determined with reference to the claims that follow. 

1-10. (canceled)
 11. A method of varying the thickening time of a class G cement used in completing a subterranean wellbore, the method comprising: preparing a slurry of the class G cement; adding ground alumina-containing spent Claus catalyst to the slurry and mixing it to form a uniform composition; and disposing the composition containing the spent Claus catalyst into the wellbore.
 12. The method of claim 11 in which the spent Claus catalyst is added to a class G cement that is in the form of a pumpable slurry.
 13. A material for use as an additive to a cementitous composition that is spent Claus catalyst in the form of substantially uniform ground particles in the size range of from 6.8 to 10.4 microns.
 14. The spent Claus catalyst material of claim 13 that has been treated to reduce any residual hydrocarbons remaining in the catalyst additive to a predetermined level.
 15. The material of claim 14 that has been subjected to a treatment selected from the group consisting of a chemical process, a thermal process, and a combination of chemical and thermal processes.
 16. The method of claim 11 in which the addition of the ground spent Claus catalyst increases the thickening time of the cement.
 17. The method of claim 11 in which the spent Claus catalyst is in the form of substantially uniform ground particles in the size range of from 6.8 to 10.4 microns.
 18. The method of claim 17 in which the spent Claus catalyst has been treated to reduce any residual hydrocarbons remaining in the catalyst additive to a predetermined level.
 19. The method of claim 18 in which the spent Claus catalyst has been subjected to a treatment selected from the group consisting of a chemical process, a thermal process, and a combination of chemical and thermal processes. 